High Hardness Alumina Ceramic Tile Ball Mill Linings
Description
Overview
Basic Info
| Model NO. | Ball Mill Liners |
| Material | Aluminum |
| Type | Wear Resistant Plate |
| Color | White |
| MOQ | 50kg |
| Delivery Time | 15~25 Days as Your Request |
| Samples | Free Samples Can Be Provided |
| Size | 150*45/50*90mm |
| Feature | Wear Resistant |
| Advantage | Interlocking Brick, Easy Installation |
| Applicable Equipments | Ball Mill |
| Item Specification | H40, H50, H60, H70, H80, H90 |
| Thickness | 40mm-90mm |
| Shape | Rectangle/Trapezoidal |
| Al2O3 Content | 92% |
| Density | 3.6g/cm³ |
| Wear Volume | <0.25 |
| Transport Package | Safe Carton with Pallet |
| Specification | as your request |
| Trademark | Ultraming |
| Origin | China |
| HS Code | 6909120000 |
| Production Capacity | 18000 Tons/Years |
Product Description
High Hardness 92% 95% Al2O3 Wear Resistant Alumina Ceramic Tile Ball Mill Linings
Alumina ceramic lining tiles for coal and other material handling and processing industries. Ceramic linings provide long-lasting solutions to the problems caused by abrasive wear and corrosion in a variety of hostile environments. Alumina ceramic linings will outlast lower grade materials commonly used to line or protect processing and material handling equipment, including Basalt, stainless steel, carbon steel and wear resistant plates, by factors of 3 to 15 times. QM X's wear resistant ceramic tiles can be cut into any shape and are easy to install and maintain. They are suitable for both wet and dry processing applications. Advanced ceramics combine high strength and toughness with extreme hardness to deliver exceptional wear resistance.
The alumina lining bricks are used as the lining in the ball mill of ceramic industry, insulator industry. Using this liner will effectively improve grinding efficiency, reduce grinding cost, and it is considered to be your best choice. · Alumina Liner for Batch Mill and Continuous Mill: Standard thickness 40 to 90 mm. with Al2O2 content 92 to 95%. · Industry : Ceramic & Insulator
Product Dimensions
| Name | Length (mm) | Width 1 (mm) | Width 2 (mm) | Thickness (mm) | |
|---|---|---|---|---|---|
| 40~90mm Thickness Lining Brick | Rectangular Brick | 150±2 | 50±1 | 50±1 | 40/50/60/70/77/90±1 |
| Trapezoidal Brick | 150±2 | 50±1 | 45±1 | 40/50/60/70/77/90±1 | |
| Half Rectangular Brick | 75±1 | 50±1 | 50±1 | 40/50/60/70/77/90±1 | |
| Half Trapezoidal Brick | 75±1 | 50±1 | 45±1 | 40/50/60/70/77/90±1 | |
| Flake Brick | 150±2 | 25±1 | 22.5±1 | 40/50/60/70/77/90±1 | |
| Special Specification Lining Bricks | 80x50x55 | 55±2 | 50±1 | 50±1 | 80±1 |
| 110mm Ling Brick | 75±1 | 45±1 | 41±1 | 110±2 | |
| 110mm Half Ling Brick | 37.5±1 | 45±1 | 41±1 | 110±2 | |
| Brick for Manhole and Drain-hole | The specification can make according to the customers' requirements. |
Product Parameters
| Character | 92 | 95 | T95 | 99 | ZTA | ZrO2 | Test Standard |
|---|---|---|---|---|---|---|---|
| Density(g/cm³) | ≥3.6 | ≥3.65 | ≥3.7 | ≥3.83 | ≥4.15 | ≥5.9 | GB/T 25995-2010 |
| Al2O3(%) | ≥92% | ≥95% | ≥95% | ≥99% | ≥75% | / | JC/T 1085-2008 |
| ZrO2 +Y2O3 | / | / | / | / | ≥21% | ≥99.8% | JC/T 1085-2008 |
| Bending Strength(MPa) | ≥220 | ≥250 | ≥300 | ≥330 | ≥400 | ≥800 | GB/T 6569-2006 |
| Compressive Strength (MPa) | ≥1050 | ≥1300 | ≥1600 | ≥1800 | ≥2000 | / | GB/T 8489-2006 |
| Fracture Toughness(MPa.m1/2) | ≥3.2 | ≥3.2 | ≥3.5 | ≥3.5 | ≥5.0 | ≥7.0 | ISO21618 IM |
| Rockwell Hardness HRA | ≥82 | ≥85 | ≥88 | ≥89 | ≥90 | ≥88 | GB/T 230.1-1996 |
| Vickers Hardness HV20(MPa) | ≥950 | ≥1000 | ≥1100 | ≥1200 | ≥1400 | ≥1100 | GB/T 16534-2009 |
| Wear Volume(cm³) | ≤0.25 | ≤0.20 | ≤0.15 | ≤0.10 | ≤0.05 | ≤0.05 | JC/T2345-2015 |